Insight into the synthesis and thermomechanical properties of "short-long" type biobased aliphatic polyesters
Category
Topical Literature Review
Department
Polymer Chemistry
Student Status
Graduate
Research Advisor
Dr. Ram Gupta
Document Type
Event
Location
Student Center Ballroom
Start Date
10-4-2025 2:00 PM
End Date
10-4-2025 4:00 PM
Description
A series of biobased "short-long" chain aliphatic polyesters having high molecular weight were successfully synthesized using dimethyl sebacate and diols with different carbon chain lengths via a two-step melt-polycondensation method by using titanium butoxide as a catalyst. The diols chain length and its odd-even effect on the structure-property relationship, crystallinity, and thermomechanical properties of the polyesters were systemically investigated. The synthesized polyesters displayed weight-average molecular weight between 23,600 to 72,900 g/mol and a maximum intrinsic viscosity of 0.933 dL/g. With increasing the diol chain length, the molecular weight of the polyesters increased linearly, except for poly (butylene sebacate) (PBS). Altogether, the "odd-even" effect of the diol chain on the crystalline (Tc)/melting temperature (Tm), and melting/ crystallization enthalpies of the polyester's were observed. Poly (pentylene sebacate) (PPeS) has the highest weight-average molecular weight of 72,900 Da, Tm of 55.4C, degradation temperature (Td, max) of about 404C, and highest storage modulus (E0 at 25 C) of 661 MPa compared to other short-chain polyesters. PBS and PPeS showed the appearance of sharp intensity peaks from XRD diffraction patterns, indicating higher crystallinity in the material, in accordance with crystallization enthalpies (AHc) values from the differential scanning calorimetry (DSC) thermograms. These fabricated bio-based polymers with 100% bio-content, low melting temperature range, rapid crystallization, and high thermal stability suggest good processability and can offer an alternative option to nonrenewable thermoplastic polyesters for potential applications.
Insight into the synthesis and thermomechanical properties of "short-long" type biobased aliphatic polyesters
Student Center Ballroom
A series of biobased "short-long" chain aliphatic polyesters having high molecular weight were successfully synthesized using dimethyl sebacate and diols with different carbon chain lengths via a two-step melt-polycondensation method by using titanium butoxide as a catalyst. The diols chain length and its odd-even effect on the structure-property relationship, crystallinity, and thermomechanical properties of the polyesters were systemically investigated. The synthesized polyesters displayed weight-average molecular weight between 23,600 to 72,900 g/mol and a maximum intrinsic viscosity of 0.933 dL/g. With increasing the diol chain length, the molecular weight of the polyesters increased linearly, except for poly (butylene sebacate) (PBS). Altogether, the "odd-even" effect of the diol chain on the crystalline (Tc)/melting temperature (Tm), and melting/ crystallization enthalpies of the polyester's were observed. Poly (pentylene sebacate) (PPeS) has the highest weight-average molecular weight of 72,900 Da, Tm of 55.4C, degradation temperature (Td, max) of about 404C, and highest storage modulus (E0 at 25 C) of 661 MPa compared to other short-chain polyesters. PBS and PPeS showed the appearance of sharp intensity peaks from XRD diffraction patterns, indicating higher crystallinity in the material, in accordance with crystallization enthalpies (AHc) values from the differential scanning calorimetry (DSC) thermograms. These fabricated bio-based polymers with 100% bio-content, low melting temperature range, rapid crystallization, and high thermal stability suggest good processability and can offer an alternative option to nonrenewable thermoplastic polyesters for potential applications.